WPC decking is a durable decking material for outdoor application.
1. Natural feeling
2. UV resistance, Waterproof, anti-slip
3. Resistant to mositure and termites
4. CE. ISO901, ISO14001, Interteck
The Eco-friendly wood plastic composite profiles we produced is made of: 60% bamboo/wood fiber, 30% HDPE, 10% chemical additives.
Main feature of mexytech wall panel:
1. Looks and feels like natural wood
2. Durable, anti-impact, wearproof, with high density
3. High capacity of UV-resistance, and color stability
4. High resistant to mositure and termites
5. Easy to be installed and low labor cost
6. Required no painting, no glue, low maintenance
7.100% recycled, environmental friendly, saving forest resources
8. Barefoot friendly, anti-slip, no cracking
9. Weather resistant, suitable from-40 to 60
Technical Data Sheet |
PROPERTY |
Test Method |
VALUE |
UNIT |
1. Density |
ASTM D792-2008 METHOD B |
1.285 |
G/CM3 |
2. Flexural Moduls |
ASTM D790-07E1 |
3070 |
Mpa |
3. Flexural Strength |
ASTM D790-07E1 |
38 |
Mpa |
4. Tensile Strength |
ASTM D638-08 |
21.08 |
MPA |
5. Water Absorption |
ASTM D570-98 |
0.8 |
% |
6. Linear Thermal Expansion Coeffiecient |
TMA |
49.82 |
UM/M °C |
7. IZOD Impact Strength |
ASTM D4812-06 |
79 |
J/m |
8. Hardness |
ASTM D2240-05 |
D/76/1 |
|
9. Curling strength |
ASTM D790 |
≥12 |
Mpa |
10. Horizontal Burning |
UL 94-1996REV.9:2006 SECTION 7 |
22 |
MM/MIN |
11. Curling Flexible Module |
ASTM D790 |
≥1600 |
Mpa |
12. Compression Strength |
ASTM D143 |
≥30 |
Mpa |
13. Grip Nail Strength |
ASTM D1037 |
≥3000 |
N |
14. Nail Withdrawal Test |
ASTM D1761 |
802 |
psi |
15. Creep Recovery Test |
ASTM D7032-SECTION 5.4 |
82.66 |
% |
16. Hot Distorted Temperature |
ASTM D648 |
≥100 |
°C |
17.UV Resistance (Light Resistance / Xenon-Arc Exposure) |
IS0105-02:2000/Amd.2:2000(E), ISO 105-A02:1993 Cor2:2005, Exposure720 hours |
Grey 4-5 grey scale Brown 4 grey scale Mahogany 4-5 grey scale Dark Walnut 4-5 grey scale |
/ |
18.Thermal Shock Test |
IEC 60068-2-14 Na: 1986, 5 cycles |
No signs of cracking, warping, chipping and discoloration |
/ |
19.Slip Resistance (Using a Horizontal Pull Slipmeter) |
ASTM F 609 |
Slip Index Reading 6.63 |
/ |
20. Material Composition |
|
Recycle Plastic 50% Natural Fibre 45% Additive 5% |
/ |
21.Mould Resistance |
ASTM F609 |
First Grade |
/ |
22.Flame Resistance |
UL 94-1996REV.9:2006 section7 |
HB |
|
PROPERTY |
Test Method |
VALUE |
UNIT |
1. Density |
ASTM D792-2008 METHOD B |
1.285 |
g / cm 3 |
2. Flexural Modul u s |
ASTM D790-07E1 |
3070 |
Mpa |
3. Flexural Strength |
ASTM D790-07E1 |
38 |
Mpa |
4. Water Absorption |
ASTM D570-98 |
0.18 |
% |
5. Linear Thermal Expansion Coefficient |
ASTM E831-06 |
49.82 |
UM/M °C |
6. IZOD Impact Strength |
ASTM D4812-06 |
79 |
J/m |
7. Hardness |
ASTM D2240-05 |
D/76/1 |
|
8.UV Resistance (Light Resistance / Xenon-Arc Exposure) |
IS0105-02:2000/Amd.2:2000(E), ISO 05-A02:1993 Cor2:2005, Exposure 720 hours |
Grey 4-5 grey scale
Brown 4 grey scale Mahogany 4-5 grey scale Dark Walnut 4-5 grey scale |
/ |
9.Thermal Shock Test |
IEC 60068-2-14 Na: 1986, 5 cycles |
No signs of cracking, warping, chipping and discoloration |
/ |
10.Mould Resistance |
ASTM F609 |
First Grade |
/ |